ultra-smooth surface for superior mechanical support
- suitable for very thin membranes
- optimal for high-differential-pressure operation and pressure transients
gradient MPL design, offering excellent water transfer and bubble removal
- →optimal for thin and low-loaded anodes (better interface)
- →more uniform reaction distribution under very high current densities
flexible structure with minimal compreession deformation
| Parameter | Unit | Nickel Fiber Felt | |
| Material | – | Pure Nickel | |
| Production Process | – | Powder-Mesh Composite Sintering | |
| Thickness | mm | 0.3 | 0.4 |
| Thickness Tolerance | μm | ±0.01 | ±0.01 |
| Surface Density | g/cm³ | 5.3~5.8 | 5.1~5.5 |
| Surface Roughness | μm | ≤12 | ≤12 |
| Maximum Pore Size | μm | 15~20 | 15~20 |
| Average Pore Size | μm | 10~12 | 10~12 |
| Porosity | % | 35~40 | 38~43 |
| Compression Ratio | %/2MPa | ≤5 | ≤5 |
| Tensile Strength | kN/50mm | 1 | 1.1 |
| Width | mm | 600 | 600 |
| Specifications | – | Customized on Demand | |
| Processing Method | – | Laser Cutting | |
| Chemical Composition | Ni % | ≥99.8 – | |
| Fe% | ≤0.02 – | ||
| C% | ≤0.03 | ||
| S % | ≤0.008 | ||
| Si % | ≤0.005 | ||
| Cu % | ≤0.001 | ||