ultra-smooth surface for superior mechanical support
- suitable for very thin membranes
- optimal for high-differential-pressure operation and pressure transients
gradient MPL design, offering excellent water transfer and bubble removal
- optimal for thin and low-loaded anodes (better interface)
- more uniform reaction distribution under very high current densities
flexible structure with minimal compreession deformation
| Parameter | Unit | Titanium Fiber Felt | ||
| Material | – | Pure Titanium | ||
| Production Process | – | Powder-Mesh Composite Sintering | ||
| Thickness | mm | 0.25 | 0.3 | 0.4 |
| Thickness Tolerance | μm | ±0.01 | ±0.01 | ±0.01 |
| Surface Density | g/cm³ | 2.8~3.0 | 2.7~2.9 | 2.6~2.8 |
| Surface Roughness | μm | ≤6.3 | ≤6.3 | ≤6.3 |
| Maximum Pore Size | μm | 12~13 | 12~13 | 12~13 |
| Average Pore Size | μm | 8~9 | 8~9 | 8~9 |
| Porosity | % | 33~37 | 35~40 | 38~43 |
| Compression Ratio | %/2MPa | ≤1 | ≤2 | ≤2 |
| Tensile Strength | kN/50mm | 0.6 | 0.7 | 1 |
| Width | mm | 550 | 600 | 600 |
| Specifications | – | Customized on Demand | ||
| Processing Method | – | Laser Cutting | ||
| Chemical Composition | Ti % | ≥99.8 | ≥99.8 | ≥99.8 |
| N % | ≤0.01 | ≤0.01 | ≤0.01 | |
| C % | ≤0.01 | ≤0.01 | ≤0.01 | |
| H % | ≤0.01 | ≤0.01 | ≤0.01 | |
| Fe % | ≤0.01 | ≤0.01 | ≤0.01 | |
| Cl % | ≤0.03 | ≤0.03 | ≤0.03 | |
| Si % | ≤0.01 | ≤0.01 | ≤0.01 | |
| Mn % | ≤0.01 | ≤0.01 | ≤0.01 | |
| Mg % | ≤0.01 | ≤0.01 | ≤0.01 | |